Low alloy steel carburization and surface microalloying process

摘要

The present invention is directed to a process for carburizing low alloy steel in a vacuum furnace in the presence of a hydrocarbon carburizing gas in combination with hydrogen wherein said carburizing gas/hydrogen combination is administered to the vacuum furnace by cyclically reducing the pressure in the furnace followed by the pulsed addition of the hydrocarbon carburizing gas consisting of an acetylene/hydrogen gas mixture in a ratio of from about 1:1 to about 1:10 at increased temperature disassociate the carbon from the gas and deposit it only on the surface of said steel and not on the surface of the furnace. The continued application of increased temperature at reduced pressure causes the deposited carbon to diffuse below the surface of the steel towards the core resulting in a carburized low alloy steel product with increased hardness, ductility and improved resistance to corrosion.

主权项

1. A process for carburizing a low alloy steel in a vacuum furnace consisting of:
a. first creating a vacuum in said furnace by reducing the pressure through the removal of the air therein followed by the introduction of a partial pressure of hydrogen to activate the surface; b. simultaneously raising the temperature of the furnace to a range of from about 1800° F to about 2500° F; c. carburizing said low alloy steel in the vacuum furnace by the pulsed addition of a hydrocarbon carburizing gas selected from the group consisting of acetylene, methane and mixtures thereof in combination with hydrogen at a pressure of from about 1 to 10 torr; d. repeating the number of pulsed addition gas carburizations to obtain the desired depth of carburization, defined as a specific hardness for a given depth of consistent hardness; f. quenching the steel by rapidly reducing the temperature to a range of from about 2010° F (1100° C.) to about 930° F. (500° C.) at an increased pressure of about 5 to 18 bar to transform the steel's core structure to an un-tempered martensite; g. placing the carburized and quenched steel in a cryogenic chamber and reducing the temperature of said chamber to −300° F(−185° C.) for sufficient time thereby stabilizing the microstructure of said steel; and h. tempering the stabilized microstructure of the steel by heating it to a temperature necessary to further develop the desired depth of carburization and core hardness.