| 摘要 |
A fluororubber composition including a polyol-crosslinkable fluororubber; a cross-linking accelerator comprising a quaternary ammonium salt; and a polyol crosslinking agent; wherein the weight ratio X (quaternary ammonium salt/polyol crosslinking agent) between the cross-linking accelerator and the polyol crosslinking agent is in a range of 0.40 to 0.60; and a production method of a cross-linked fluororubber product, comprising the steps of: previously polyol-crosslinking, as required, the fluororubber composition; and subsequently heat treating the polyol-crosslinked composition, in a temperature range of 200° C. to 300° C. for 0.1 to 48 hours. The fluororubber composition has surface has a lower friction coefficient, and the surface roughness of the cross-linked fluororubber product can be increased without applying a treatment to a mold.
|