Manufacture of materials and workpieces for components in nuclear plant applications

摘要

A method of producing austenite steel for use in the radiation zone of a nuclear reactor. The method comprising the steps of forming the austenite steel with about 17% by weight chromium, about 9 to 11.5% by weight nickel, about 0.04% by weight carbon, and iron impurities whose content of silicon is about 0.1% by weight and whose total content of sulfur and phosphorous is less than 0.03% by weight; and exposing the austenite steel to a temperature treatment at a temperature less than 1150 DEG C. to produce a fine grain lattice with grain diameter features under approximately 20 mu m.