The non-acicular modified maghemite and magnetite have high coercivity of, for the maghemite, up to 2200 Oe, saturation and residual magnetization of 63-85 emu/g and 43-52 emu/g, respectively; for the magnetite, the corresponding values are 800-1600 Oe, 82-87 emu/g, and 44-51 emu/g, respectively; while retaining same squareness ratio and same chemistry with conventional iron oxides, fine particle size of around 50 nm, easier dispersion and coating, invaried properties after curing, and low value of temperature coefficient of coercivity (0.24-0.37%/ DEG C. for the maghemite and 0.20-0.33%/ DEG C. for the magnetite), have been invented. They are thus especially suitable for high density recording. The modified maghemite and magnetite are prepared by precipitating from aqueous solution containing Fe, Mn, Co and Zn ions at proper ratio using an organic alkali as precipitant, followed by specific heat treatment sequences.
|