<p>An abrasive sheet having a high flexibility, mechanical strength and heat resistance, comprises (A) a matrix comprising an aromatic polyimide resin and (B) abrasive grains having an average size of 65 - 150 mu m and evenly dispersed in an amount of 2 to 50% by weight in the matrix, and is produced by forming a thin liquid layer from a dispersion comprising an aromatic polyamic acid solution with a rotation viscosity of 3000 to 6000 poises at 30 DEG C and the above-mentioned abrasion grains dispersed in the solution, and dry-solidifying the liquid layer of the dispersion while imidizing the aromatic polyamic acid to a corresponding aromatic polyimide, the abrasive sheet having a thickness of 1.1 to 3.0 times the average size of the abrasive grains. <IMAGE></p> |