| 摘要 |
A heat-dissipating sheet having a density of 2.0 g/cm 3 or more and an in-plane thermal conductivity of 580 W/mK or more, which comprises carbon black uniformly dispersed among fine graphite particles, a mass ratio of fine graphite particles to carbon black being 75/25 to 95/5, and the carbon black being composed of channel black and ketjen black and/or acetylene black is produced by applying a dispersion of fine graphite particles, carbon black and an organic binder in an organic solvent to a surface of a die, drying it; burning the resultant resin-containing composite sheet to remove the organic binder; and then pressing the resultant composite sheet of fine graphite particles and carbon black for densification. |