| 摘要 |
A metal surface treatment method for a metal base material in order to improve the uniformity of a cathodic electrodeposition coating film, the method including: a surface treatment step for forming a chemical conversion film on a metal base material by contacting the metal base material with a metal surface treatment composition including zirconium and/or titanium ions and an adhesive imparting agent characterized in being at least one selected from the group consisting of (A) silicon-containing compound, (B) adhesive imparting metal ion, and (C) adhesive imparting resin; and a heating/drying step to heat and dry the metal base material, on which the chemical conversion film is formed, at 60° C. to 190° C. for at least 30 seconds. |
| 主权项 |
1. A surface treatment method for improving the uniformity of a cathodic electrodeposition coating film, wherein the surface treatment method forms a chemical conversion film on a metal base material by contacting the metal base material with a metal surface treatment composition comprising
at least one of zirconium ions or titanium ions; at least one adhesive imparting agent selected from the group consisting of (A) silicon-containing compound which is at least one of a silane coupling agent that is an aminosilane or hydrolysis-polycondensate of the aminosilane, having at least one amino group, (B) an adhesive imparting metal ion selected from the group consisting of magnesium, zinc, calcium, aluminum, gallium, indium, copper, iron, manganese, nickel, cobalt, silver, and tin, and (C) adhesive imparting resin selected from the group consisting of a polyamine compound and a melamine resin, and
wherein the surface treatment method comprises a step of surface treatment whereby the metal surface treatment composition comes into contact with the metal base material, and a step of post-treatment of heat-treating the metal base material after the step of surface treatment, and wherein said post-treatment process is a process of heat-treating the metal base material under atmospheric pressure or pressurized conditions in hot water at 60° C. to 120° C. for 2 seconds to 600 seconds, and wherein there is applied thereafter a cathodic electrodeposition coating film onto fine portions of the metal base material with curves and bag portions, wherein the total amount of the zirconium and titanium ions in the metal surface treatment composition is 10 ppm to 10000 ppm based on metal element content, wherein the total amount of the aminosilane, the hydrolysis-polycondensate of the aminosilane, or both, in the metal surface treatment compositions ranges from 1 ppm to 2000 ppm based on silicon element content, wherein the ratio of the total amount of zirconium and titanium elements to the total amount of silicon element contained in the aminosilane, the hydrolysis-polycondensate of the aminosilane, or both, is 0.5 to 500, wherein the metal surface treatment composition has a pH of 1.5 to 6.5, wherein the adhesive imparting metal ion is present in an amount of from 1 ppm to 5000 ppm in the metal surface treatment composition, and wherein the polyamine compound comprises at least one constituent unit represented by the chemical formula and wherein the ratio of the total amount of the zirconium and/or titanium ions to the mass of the polyamine compound is 0.1 to 100, and wherein in the chemical formula (3), R1 is an alkylene group having 1 to 6 carbon atoms, R2 is a substituent group represented by the following chemical formulas (4) to (6) shown below, and R3 is a hydroxyl group, an alkoxy group having 1 to 6 carbon atoms or an alkyl group having 1 to 6 carbon atoms, and in the chemical formula (6), R6 is a hydrogen atom, an aminoalkyl group having 1 to 6 carbon atoms or an alkyl group having 1 to 6 carbon atoms, and R7 is a hydrogen atom or an aminoalkyl group having 1 to 6 carbon atoms. |