Method for preparing the matte anti-fingerprint stainless steel decorative plate |
摘要 |
The present invention provides a method for preparing a matte anti-fingerprint stainless steel decorative plate. The method comprises the steps of: 1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing acrylic resin, a film forming material, an inorganic nano-filler, a solvent and an auxiliary agent, wherein the film forming material comprises the following ingredients based on the weight ratio: 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, 5-15 parts of epoxy resin, 1-5 parts of an inorganic nano-filler, 40-50 parts of a solvent and 10-20 parts of an auxiliary agent; and 1-8 parts of a matting agent and 1-8 parts of an anti-settling agent are added; and 2) performing a spray coating using the polymer coating material, wherein a coating film has a thickness of 1.5-2.5 μm, the precision of the atomization air pressure of a spray gun is controlled at ±0.1 bar during spray coating, and the coating is dried to obtain a finished product and then a matte anti-fingerprint stainless steel decorative plate which has a high-standard matte and anti-fingerprint index is prepared. |
申请公布号 |
US2015267072(A1) |
申请公布日期 |
2015.09.24 |
申请号 |
US201414548847 |
申请日期 |
2014.11.20 |
申请人 |
HAIMEN SENDA DECORATION MATERIAL CO., LTD. |
发明人 |
HUANG LIXIN;HONG LIANG;SANG ZHIHONG;CHEN GANG;JIANG HUI |
分类号 |
C09D133/08;B05D3/00;B05D3/02;B05D1/02 |
主分类号 |
C09D133/08 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for preparing a matte anti-fingerprint stainless steel decorative plate, comprising:
1) selecting a polymer coating material, wherein the polymer coating material is formed by mixing acrylic resin, a film forming material, an inorganic nano-filler, a solvent and an auxiliary agent, and wherein the film forming material comprises the following ingredients based on the weight ratio: 30-50 parts of acrylate composite resin, 5-20 parts of amino resin, 5-15 parts of epoxy resin, 1-5 parts of an inorganic nano-filler, 40-50 parts of a solvent and 10-20 parts of an auxiliary agent; and 1-8 parts of a matting agent and 1-8 parts of an anti-settling agent are added; 2) performing a spray coating using the polymer coating material to form a coating film, wherein the coating film has a thickness of 1.5-2.5 μm, and a precision of the atomization air pressure of a spray gun is controlled at ±0.1 bar during the spray coating; and drying the coating is dried to obtain a finished product. |