THE THERMOPLASTIC ACRYLIC RESIN FOR PVDF BINDER WHICH IS APPLICABLE ON AUTO TOP COATINGS FOR PRE-COATED METAL SYSTEM AND ITS SYNTHETIC METHOD WITH SOLUTION POLYMERIZATION |
摘要 |
PURPOSE: An acrylic resin for a polyvinylidene fluoride resin binder is provided to have excellent durability, weatherability, flexibility, and exterior appearance. CONSTITUTION: An acrylic resin for a polyvinylidene fluoride resin binder comprises 15-20 parts by weight of methyl methacrylate, 8-12 parts by weight of n-butyl methacrylate, 5-10 parts by weight of 2-ethyl hexyl acrylate, 1-5 parts by weight of 1,6-hexanedioldiacrylate, 0.5-1 parts by weight of t-butyl amino ethyl methacrylate, 0.5-0.9 parts by weight of t-amylperoxy-2-ethyl hexanoate, 0.5-0.9 parts by weight of t-butyl peroxybenzoate as a polymerization initiator, 50-70 parts by weight of toluene or butyl acetate as a reaction solvent, and 30-50 weight% of solid phase.
|
申请公布号 |
KR20130040277(A) |
申请公布日期 |
2013.04.24 |
申请号 |
KR20110104919 |
申请日期 |
2011.10.14 |
申请人 |
PPG INDUSTRIES (KOREA) INC. |
发明人 |
NAM, JOON HYUN;KIM, DONG GAN;NOH, SUENG MAN;PARK, CHAN NAM;HAN, JONG HEE;JEONG, HO CHEOL |
分类号 |
C08L33/04;C08F2/04;C08F20/10;C09D133/04 |
主分类号 |
C08L33/04 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|